Adsorption behavior of rhamnolipid modified magnetic Co/Al layered double hydroxide for the removal of cationic and anionic dyes

Scientific Reports volume 12, Article number: 14623 (2022) Cite this article 1980 Accesses 32 Citations 1 Altmetric Metrics details In the present research, magnetic rhamnolipid-Co/Al layered double

Scientific Reports volume 12, Article number: 14623 (2022) Cite this article

1980 Accesses

32 Citations

1 Altmetric

Metrics details

In the present research, magnetic rhamnolipid-Co/Al layered double hydroxide (MR-LDH) was synthesized to uptake methylene blue (MB) and reactive orange 16 (RO16) from aqueous solution. The main parameters, including pH, adsorbent dosage, contact time, and initial analyte concentration, were optimized to achieve the best adsorption efficiency. Accordingly, the elimination of MB on MR-LDH is improved in the basic medium due to the electrostatic interactions between the negative charge of MR-LDH and the positive charge of MB dye. In contrast, the acidic medium (pH = 3) was favored for RO16 adsorption because of hydrogen bonding between the protonated form of azo dye and protonated hydroxyl groups at the surface of MR-LDH. The calculated maximum adsorption capacities for MB and RO16 were 54.01 and 53.04 mg/g at 313 K, respectively. The Langmuir model, which assumes monolayer adsorption on the adsorbent surface, provides the best explanation for the adsorption of both dyes (R2 = 0.9991 for MB and R2 = 0.9969 for RO16). Moreover, the pseudo-second-order kinetic model best described the adsorption process for MB (R2 = 0.9970) and RO16 (R2 = 0.9941). The proposed adsorbent maintains stable adsorption performance for four consecutive cycles. After each adsorption process, MR-LDH is easily separated by an external magnet. The findings show that MR-LDH was found to be an excellent adsorbent for the removal of both cationic and anionic organic dyes from aqueous solutions.

As a result of the continuous release of pollutants into the environment especially water, the removal of the industrial effluents, including leather, printing, textile, refineries, plastic, and petroleum industries, has become one of the global challenges1,2,3,4,5. Due to their slow decomposition and toxicity, dyes can cause irreparable damage to the environment ecosystem and lead to severe problems in aquatic animals and humans6,7,8.

Textile dyes are classified according to their functional groups: nitro, nitroso, azo, anthraquinone, indigo, sulfur, and so on9,10. These dyes are recalcitrant, non-biodegradable, bioaccumulative, toxic, and carcinogenic and have harmful effects on the environment, even at low concentrations11,12,13,14. It is also common practice to categorize dyes according to the charge that is left on their particles after dissolution in an aqueous medium. These categories include anionic (which includes direct, acidic, and reactive dyes), cationic (which includes all basic dyes), and non-ionic (dispersed dyes)15,16.

Methylthioninium chloride, commonly called methylene blue, is a water-soluble non-biodegradable cationic dye belonging to the thiazine family with a pka of 3.8. Reactive Orange 16, a highly water-soluble recalcitrant and xenobiotic monoazo dye with a pka of 3.75, is inherently hazardous and has carcinogenic and mutagenic effects in humans17,18,19,20. Therefore, removing dyes from wastewater is considered an environmental challenge21,22.

Diverse techniques have been employed to eliminate synthetic dyes from pollutant water including filtration, flocculation, biological treatment, coagulation, adsorption, extraction, membrane separation, photocatalytic degradation, and oxidation23,24,25,26. Some of these traditional methods have been restricted due to being complex, time-consuming, and uneconomical27. Thus, finding the most efficient and simple dye wastewater treatment method is necessary28. In recent decades, adsorption has garnered a lot of attention as a more preferred method due to its flexibility and simplicity in design, as well as its insensitivity to toxic contaminants and its lack of generation of toxic materials2,25,29,30,31. The adsorption efficiency highly depends on the properties of the adsorbent30. Tradition adsorbents including clay, biochar, chitosan, zeolite, silica, or synthetic adsorbents including active carbon, polymers, mesoporous carbon material, waste rubber tires or filter membranes have been tested to remove contaminants from wastewater32,33,34.

One of the potent adsorbents is a hydrotalcite-like layered structure known as layered double hydroxide (LDH), bearing an adjustable usage density and significant chemical uniformity35. Due to the versatility of structural composition, morphology, and several synthesis strategies, LDH can be easily manipulated for specific adsorbent processes with improved performance36,37. Its structure consists of divalent and trivalent metal ions in the layers with guest charge-balancing anions intercalated between the layers36,37.

This structure greatly contributes to its anionic exchange capability depending on synthetic conditions and the application goal38. The general formula for LDH is given as [M1-x2+Mx3+(OH)2]x+[An-]x/n·zH2O, in which M2+ and M3+ display divalent cation (e.g. Mg2+, Ca2+, Zn2+, Ni2+, Cu2+, Co2+, and so on.), trivalent cation (e.g. Al3+, Fe3+, Cr3+, Ga3+), respectively39,40. The common anions that present interlayer of LDHs are sulfate, carbonate, nitrate, hydroxide, chloride, and bigger anion like polyoxometalates41,42.

The total charge of LDHs is positive because the anion's negative charge helps hold the positively charged brucite-like sheets through electrostatic attractions43,44. Various features of these layered materials like high specific surface area, low cost and facile synthesis, ion-exchange capability, and swelling abilities make them suitable for use as a dye adsorbent45,46,47. There is a significant class of amphiphilic molecules known as surfactants. These molecules have head and tail parts, and they have the ability to attract both polar and non-polar species. They act as a bridge between the air and the liquid as they accumulate on the surface while simultaneously lowering the surface tension of the species they accumulate on48. Rhamnolipids (RL), anionic glycolipid biosurfactants, are provided by various bacteria. These materials are a potentially good alternative to synthetic chemical surfactants for pharmaceuticals and cosmetics owing to their advantages, including low toxicity and being environmentally friendly49. Rhamnolipids contain 3-(3-hydroxyalkanoyloxy)alkanoate, with hydrophobic acyl chains attached to a hydrophilic moiety which is created by one or two rhamnose molecules50,51. Textile dyes, for instance, can benefit from an expanded assessment of biosurfactants' application, especially rhamnolipid-based ones49.

Recently, a series of LDH with various metals (Mg, Zn, Mn)-Fe molar ratios were prepared to eliminate dye molecules from wastewater52,53. Results showed that the Mg-Fe molar ratio of 3:1 was the optimal efficiency (Mg-Fe LDH: 71.94 mg/g at 298.15 K) for MB removal3. In another study, a 3D Mg/Al LDH was synthesized to uptake the anionic Acid Orange 7 (AO7) as well as cationic MB by employing sodium dodecyl sulfate as a modifier. The maximum removal capacities were reported for AO7 and MB as 485.6 and 58.3 mg/g, respectively. Moreover, the regeneration experiments showed that Mg/Al LDH could be recycled five times. Authors also claim that their adsorbent provided a promising platform for removing ionic dyes using 3D-LDHs54,55.

Herein, by employing magnetic rhamnolipid and Co/Al LDH, a powerful platform was prepared to assess the removal rate of two organic dyes, i.e., MB and RO16, from effluent wastewater for the first time. The proposal platform, namely MR-LDH displayed the significant capability to remove both dyes from the aqueous solution. Moreover, the magnetic nature of the adsorbent provides a suitable condition for taking the spent adsorbent out from the working solution for repetitive cycles.

Rhamnolipid (> 90%) and metal salts (i.e., Fe, Co, and Al salts 99.9%) were provided from Sigma and Aldrich Company, respectively. Other chemicals, including sodium acetate (99.5%), ethylene glycol (99%), MB (99%), RO16 (99%), and formamide (99.9%), were obtained from Merck Company in analytical grade. All materials were employed with no purification.

Different methodologies were used to establish the sample's composition, including powder X-ray diffraction (XRD) with monochromated Cu–Kα radiation (λ = 1.54056 A). A Nicolet 100 Fourier transform infrared (FTIR) spectrometer was used to collect the FT-IR spectroscopic data, which covered the wavelength range of 400–4000 cm-1. The shape and particle size of the particles were also determined using transmission electron microscopy (TEM) (TEM Philips EM208S 100 kV). Another tool used to evaluate the morphology of the materials was the scanning electron microscope (SEM) TESCAN VEGAII (Czech Republic). Using a vibrating sample magnetometer, the magnetic characteristics of the samples could be determined. Utilizing an ultraviolet–visible spectrophotometer, the maximum absorbance wavelengths were used to determine the quantities of dyes in the aqueous solutions (DR6000).

3.25 g of FeCl3·6H2O and 8.64 g of CH3COONa·3H2O were dissolved in 80 mL of ethylene glycol at 313 °C under solvothermal conditions to produce the MR-LDH. A light brown solution appeared. Then, it was sealed with a polytetrafluoroethylene liner. After that, the reactor containing the as-prepared solution was heated at 473 K within 8 h. The obtained powder was collected followed by washing with distilled water and ethanol several times to eliminate impurities, followed by drying for 9 h at 333 K. The final black powder is magnetic Fe3O4. Under sonication at 318 K, the urea method was carried out to go on the process. According to this technique, Al(NO3)3·9H2O and Co(NO3)2·6H2O were dissolved in distilled water, resulting in 0.5 M solution. 3 g/L of obtained Fe3O4 was added to the solution to create MR-LDH. Then, after 10 to 12 min, it was sonicated. A water-ammonia solution (volume ratio 4:1) was added to the suspension to enhance precipitation at pH 9–10. The solution was filtered under vacuum after 20 h at ambient temperature. Then, it was washed four times and dried at 353 K within 24 h to produce the magnetic product powder.

For obtaining nanocomposite of MR-LDH, delaminating–reassembling method is employed. Accordingly, 0.4 g of the magnetic core in formamide (25 mL) was stirred, followed by sonicating within 20 min. Then, 20 mL of the suspension was mixed with 20 mL of RL/NaOH 0.1 M aqueous solution containing 1 g of rhamnolipid under weak stirring within 30 min. The suspension was then separated using a magnet and rinsed three times with distilled water/ethanol. Finally, the MR-LDH powder was then produced by drying the product at 353 K. Schematically, the synthesis process of Fe3O4@RL-LDH illustrates in Fig. 1.

The synthesis process of Fe3O4@RL-LDH.

The powder XRD technique was employed to characterize the as-prepared samples. The patterns of all materials are in accordance with simulated pattern (Fig. 2a). The typical peaks of LDH were seen at the diffraction plans (003), (006), (012), (110), and (113). The reflections of (003) and (006) are aroused by hydrotalcite-type material. The strength of the peaks is proportional to the degree of crystallinity of the sample along a certain axis of the sample. Furthermore, the significant peaks in magnetic nanoparticle patterns, i.e., Fe3O4, at 2θ = 30.2°, 35.5°, 43.3°, 53.6°, 57.5°, and 62.5° are attributed to the reflection planes of (220), (311), (400), (422), (511), and (440), respectively. The distance between the layers of MR-LDH obtained 3.44 nm according to the (003) diffraction peak, which is greater than that of one of the Co/Al-LDH (0.89 nm). This difference is due to the presence of the RL anion within the layers. Furthermore, In XRD patterns of the magnetic core and MR-LDH, characteristic peaks of Fe3O4 and LDH were also observable.

XRD pattern (a) and FTIR spectra (b); (a) LDH, (b) Fe3O4, (c) Magnetic Co/Al LDH, and (d) MR-Co/Al LDH.

FTIR spectra of the materials are demonstrated in Fig. 2b. The peaks at 800 cm-1 were attributed to the stretching vibrations links between metal and oxygen (M–O) in the samples. Surface OH of Co/Al LDH layers and hydroxyl stretching vibration of coordinated water were observable at 3500 cm-1 in all materials' broadband spectra. The peak of LDH at 2900 cm-1 explains the interaction of interlayer CO32 and water molecules. The stretching vibration of LDH was discovered to be the interlayer nitrate anion at 1385 cm-1. The vibration of the Fe–O bond is depicted in the pattern of Fe3O4 as a peak at 582 cm-1, but it is diminished in the composites' spectra. The vibration mode of the nitrate anion in MR-LDH disappeared, but the C-H stretching vibration caused the new bands at 2928 and 2856 cm−1.

SEM and TEM pictures of the magnetic core and as-prepared MR-LDH are shown in Fig. 3. As illustrated, LDH before modification with RL has a lamellar structure and remains in this shape in the presence of RL. According to the TEM images, the Fe3O4 core is encapsulated by LDH nanosheets resulting in a core–shell composite structure. The composite's average size was calculated to be around 100 nm. Furthermore, Fig. 3 proves that RL was placed between the layers of LDH, leading to aggregating the final composite.

SEM and TEM images of magnetic LDH (a), (c) and MR-LDH (b), (d).

Figure 4 provides the magnetization curves of all the samples. An acceptable super-paramagnetic property is observable, according to the plots. Compared to magnetic Fe3O4, the saturation magnetization of the core and MR-LDH declines because of the addition of nonmagnetic moieties (i.e., LDH sheets). The samples' hysteresis and coercivity have faded away. Furthermore, because of the presence of RL within the layer, the amount of saturation magnetization of MR-LDH is significantly lower than the value of magnetic LDH.

Magnetization curves of (a) Fe3O4, (b) magnetic LDH, and (c) MR-LDH.

The surface charge of the adsorbent and adsorbate is highly dependent on the pH of the solution. This implies that the deprotonation (or protonation) of a dye must be considered30. The pH can change the ionization degree, the adsorbent surface charge, and the molecular structures of the adsorbates. So, the solution pH determines the kind of interaction between the adsorbent and dyes through the ionization of species in the solution. As depicted in Fig. 5a, with decreasing pH to the acidic range, the adsorption efficiency of MB declines. Based on the plot, the optimum pH for MB removal was found to be 9, which will be used for further experiments. Considering the MB structure, it bears π-conjugated electron density, but the proposal adsorbent does not contain π-conjugated electrons leading to ruling out π-π stacking interaction. While positively charged adsorbent may interact with MB as cation-π interaction effectively in the upper and bottom of the MB plane. Moreover, hydrogen bonding can form between hydroxides of the adsorbent and the nitrogen site of MB, leading to effective adsorption. But, the scenario is completely different for RO16 adsorption. It does not bear an expanded π-conjugated structure. As illustrated in Fig. 5a, adsorption efficiency reached the highest value when pH was reduced to 3. At low pH, this dye ionizes into anion form, affecting electrostatic interaction with the positively charged adsorbent. Furthermore, the existence of hydroxyl groups in the RO16 structure results in hydrogen bonding with OH sites of the proposal adsorbent. As a result, pH 3 was chosen as the best value for subsequent studies aimed at RO16 removal. Furthermore, the point of zero charges (pHpzc) of the adsorbent was obtained to be equal to 7.6 (Fig. 5b). The proper interaction behavior of MR-LDH for MB and RO16 adsorption can be described using pHpzc. MR-LDH is negatively and positively charged at pH > pHpzc and pH < pHpzc, respectively. Thus, at pH > pHpzc the electrostatic interaction between adsorbent and analyte is repulsion and attraction for RO16 and MB, respectively. On the other hand, at pH < pHpzc, it happens completely the opposite way.

(a) The effect of pH of the solution on the MB and RO16 adsorption and (b) determination of pHpzc.

The adsorbent dosage also affects the adsorption behavior. Generally, increasing the adsorbent dosage leads to increasing the adsorption because more active sites will be accessible for the analyte. In contrast, higher dosages may cause adsorbent agglomeration and lose the active sorption sites. In other words, the adsorbent seeds stack to each other and do not let the analyte interact with the adsorption sites. Therefore, finding the optimized adsorbent dosage is one of the major stages in contaminant removal until they can perform separately. Due to the adsorbent's unsaturated active sites, the adsorption capacity is increased and accelerated. The plots of the removal efficiency of MB and RO16 at different adsorbent dosages are drawn in Fig. 6. According to the findings, MB removal efficiency increased as adsorbent dosage increased up to 15 mg of MR-LDH. Then, the process reaches equilibrium. In the case of RO16 adsorption, 10 mg was the optimal adsorbent dosage. After the optimum values, adding more adsorbents leads to agglomeration of the active sites on the adsorbent, decreasing the adsorption efficiency56. Therefore, adjusting the adsorbent dosage to optimum value is also beneficial from the economic aspect.

The effect of adsorbent dosage on the MB and RO16 removal.

Another aspect that needs to be taken into consideration is the effect of the initial dye concentration. Notably, an increase in dye concentration has perceptible effects up to a critical limit. Additionally, the adsorbent tends to adsorb high concentrations of dye molecules that are proportional to the accessible sorption sites on the adsorbent's surface. As the surface saturation is occurred, remarkable dye adsorption will be observed. Thus, the adsorption of MR-LDH toward MB under various dye concentrations (5, 8, 10, 12, and 15 mg/L) are displayed in Fig. 7a. Accordingly, as the concentration of MB rises from 8 to 15 mg/L, the ability of MR-LDH to bind to it decreases. 8 mg/L was the best initial concentration for MB uptake (Fig. 7b). In the case of RO16 removal, the highest adsorption efficiency was observed in 10 mg/L initial concentration. After optimum values, the active sites of the adsorbent were saturated, leading to decreasing the adsorption efficiency. Because the vacant space between the layer of MR-LDH is limited. By replacement of interlayer anions of the adsorbent with contaminants, the adsorption is performed. Therefore, this space can accept the optimum amount of analyte, leading to effective adsorption. In this regard, after saturation of active sites of the interlayer of MR-LDH, further contaminants cannot diffuse onto the adsorbent.

The effect of initial dye concentration on the (a) MB and (b) RO16 removal.

Increasing contact time can negatively and/or positively affect the adsorptive removal of dyes. During the upward part of the plot, the contact of dyes and adsorbent leads to effective adsorption because the active sites have not been saturated yet. When the equilibrium between the sorption sites and dye molecules is established, additional reaction time does not affect adsorption because the sorption sites become saturated during contact time, and no more unoccupied space is available for additional dye adsorption. The optimum contact time for dye removal is shown in Fig. 8; in this case, MR-LDH was able to remove 75% of the initial concentration of MB after only 150 min. Then, the adsorption processes remained unchanged within passing time illustrating the active sites of MR-LDH were saturated. In a report, magnetic-based polymers Core@double-shell structured magnetic halloysite nanotube was eliminated MB during 3 h57. For RO16, in less than 40 min, about 97% of the analyte was taken up and no more dye remained in the solution. But in previous literature, the time of 50 min was reported for removal of RO16 by chitosan-fly ash/Fe3O432.

The effect of contact time on the MB and RO16 removal.

In Fig. 9, the optimization of temperature was carried out. As can be seen, for both dyes, 40 ºC has the best result and leads to the highest adsorption efficiency. Since with increasing the temperature, the adsorption is elevated, it can be said that both reactions are endothermic.

The effect of temperature on the MB and RO16 removal.

To analyze experimental data from the adsorption process, the distribution of the dyes among the aqueous solution and MR-LDH at the adjusted temperature and discuss the equilibrium of adsorption, some well-known adsorption isotherm equations, including Freundlich, Langmuir, and Temkin will be introduced here58. Firstly, the non-linear form of the Langmuir isotherm is presented as Eq. (1):

where qe (mg/g) represents the equilibrium adsorption capacity and qm (mg/g) is the maximum adsorption capacity. KL (L/mg) denotes the model's constant. With Eq. (2), the Langmuir isotherm's basic properties are introduced as a dimensionless equilibrium parameter (RL):

where C0 (mg/L) shows the highest initial concentration of the analyte, and KL is the Langmuir constant. RL demonstrates the type of adsorption to be either unfavorable (RL > 1), favorable (0 < RL < 1), linear (RL = 1) or irreversible (RL = 0). This isotherm assumes homogeneous adsorption and single-layer coverage of the MR-LDH surface by dye without any interaction between analyte molecules.

An empirical model for surface heterogeneity and an exponential distribution of the energy and sorption sites of the adsorbent is the Freundlich isotherm. The Freundlich isotherm as a reversible adsorption model is not limited to monolayer formation, which is shown in Eq. (3):

where KF (mg/g)/(mg/L)n and n are described Freundlich constant. The value of n illustrated that the adsorption is favorable and placed in the range of 1 to 10.

The adsorption heat between dyes and MR-LDH is determined by the Temkin isotherm. Temkin isotherm assumes interaction between dyes and MR-LDH which is presented as Eq. (4):

where R is the gas's universal constant (i.e., 8.314 J/mol. K), T (K) is the temperature, bT (J/mol) points to the adsorption heat constant of Temkin and KT is the Temkin isotherm equilibrium binding constant (L/g).

The adsorption isotherm of MB and RO16 for MR-LDH was assessed at 298 K and the data were analyzed by Freundlich, Langmuir, and Temkin models, respectively. Figure 10 demonstrates the adsorption capacity as a function of the equilibrium RO16 and MB concentration using a non-linear fitting method. In the case of MB removal, the adsorption process followed the Langmuir model, indicating that the adsorption is monolayer and takes place on the particular homogenous sites of the MR-LDH surface. The correlation coefficients of the Langmuir isotherm model were calculated equal to 0.9991, which is significantly higher than the R2 values for Freundlich (0.9841) and Temkin (0.9915) models. The Langmuir model has been found to be the best fitting model for describing the adsorption pathway in some previous studies for MB removal. The removal of MB by AC made from coconut leaves with an adsorption capacity of 149.3 mg/g, AC made from lemon peels/sodium alginate with an adsorption capacity of 841.37 mg/g, magnetite/MWCNTs with an adsorption capacity of 55 mg/g, and so on, can be noted among them. In the case of RO16 adsorption, the corresponding plot displays that the adsorption follows the Langmuir model either59,60,61. Therefore, the adsorption of RO16 onto MR-LDH was also monolayer uniform adsorption and no more interaction between the dye molecules was not formed62. The correlation coefficient of the Langmuir model for RO16 adsorption was calculated as 0.9969, further proving the fitting model. The correlation coefficients of two other models, including Freundlich (0.9827) and Temkin (0.9885), are relatively lower than the Langmuir value. In Table 1, all numerical investigations of all adsorption models are observable.

Isotherm fitted curves (non-linear) of (a) MB and (b) RO16 adsorption.

Kinetic parameters are mainly considered to define the adsorption efficiency because fast kinetics is of great significance in aqueous phase adsorption. To evaluate the kinetic parameters of MR-LDH, the collected experimental results were fitted with four common kinetic models, including pseudo-first-order, pseudo-second-order, Elovich, and Fractional kinetic models. The pseudo-first-order kinetic model is presented in Eq. (5):

After the integration of the previous equation, the pseudo-first-order is illustrated in the linear form (Eq. 6):

The sorption kinetics also was described by the pseudo-second-order model, which is presented by Eq. 7:

Following the integration of the above equation, the pseudo-second-order model is denoted by Eq. 8:

where k1 and k2 are the rates constant of the pseudo-first-order model (min−1) and pseudo-second-order model (g/mg.min), respectively.

The third one is Elovich as follows [Eq. (9)]:

The non-linear form of the fractional power equation is as follows [Eq. (10)]:

where the antilog of intercept leads to the value of constant kp. vp is a constant which is commonly less than unity if adsorption kinetic data fit well into the power function model. qt is the quantity of analyte adsorbed at time t63.

The plots (non-linear curve fitting) and results obtained from the mentioned models are provided in Fig. 11 and Table 2 for both dyes, respectively. In the case of MB removal, by comparing the correlation coefficients, the pseudo-second-order (R2 = 0.9970) was superior to those of the others, including pseudo-first-order R2 of 0.9769, and Elovich of 0.9931 and fractional of 0.9780. In addition, the calculated equilibrium capacity value (qe,cal = 48.86 mg/g) using the pseudo-second-order was closer to the corresponding experimental one (qe,exp) compared to those of the other models. Thus, the adsorption of MB dye by MR-LDH may be well described by a pseudo-second-order kinetic model. Consequently, electrons are shared or exchanged between the MR-LDH and the positively charged MB dye taken place during chemisorption. In recent research, egg shells derived from industrial waste were utilized to adsorb MB, demonstrating an adsorption capacity of 94.9 mg/g, which was consistent with the pseudo-second-order kinetic model64. In another study, finger-citron-residue-based activated carbon removed MB with a capacity of 581.40 mg/g, also fitting with the pseudo-second-order kinetic model65. In the case of RO16 adsorption, identical outcomes were observed again. As shown in Table 2, the value of R2 for the pseudo-second-order (R2 = 0.9941) is closer to 1.0 than that of the pseudo-first-order, demonstrating the applicability of the pseudo-second-order model to describe the rate of adsorption, which assumes that chemisorption may be the rate-limiting step. In a different study that has already been published, a cross-linked composite of natural and synthetic clays with a capacity of 190.97 mg/g for RO16 adsorption was produced66. Moreover, another adsorbent for RO16 adsorption with a capacity of 66.9 mg/g was chitosan-fly ash/Fe3O4, which was fitted with the pseudo-second-order kinetic model32. Authors claimed that electrostatic attraction, H-bonding, and π–π stacking interactions are responsible for the adsorption process as the subset of the chemisorption category.

Kinetic fitted curves (non-linear) of (a) MB and (b) RO16 adsorption.

In general, hydrogen bonds, π–π stacking, electrostatic attraction, base-acid interactions, van der Waals forces, and hydrophobic contact are the main mechanisms involved in the adsorption of water contaminants on adsorbents. Replacement of analytes, and dyes in this case, with the interlayer anion of MR-LDH is the main driving force of the adsorption route. In this approach, various interactions facilitate the adsorption phenomenon. In the case of MB removal, the π-conjugated electrons can interact with positively charged MR-LDH as π-cation interaction. Lacking the π-conjugation plane in MR-LDH rules out the π-π stacking interaction between them. As the adsorption took place at basic pH, partially deprotonation of the LDH can conduct electrostatic interaction with MB, which accelerates the adsorption process. In the acidic pH of adsorption for the RO16 removal, RO16 was partially protonated, which rules out the electrostatic attraction with the adsorbent. In this case, the presence of π electrons density can form π-cation interaction between RO16 and MR-LDH. Moreover, the presence of OH groups can perform hydrogen bonding with hydroxides of MR-LDH. Schematic illustrations of adsorption are provided in Fig. 12.

The removal mechanism of (a) MB and (b) RO16 by MR-LDH nanocomposite.

In addition to the explanations provided, the possibility of diffusion from the solution containing adsorbate to the solid surface can be checked by the Weber-Morris intra-particle diffusion equation. Basically, the intra-particle diffusion equation is used to investigate the controlling step of the adsorption process. The linear form of the intra-particle diffusion equation is expressed as Eq. (11)67:

In the mentioned equation, kid (mg/g min1/2) and I (mg/g) represent the intra-particle diffusion rate constant and a constant related to the boundary layer thickness, respectively. Figure 13 shows the changes in adsorption capacity vs. t0.5. As it is known, in general, the changes in adsorption capacity with t0.5 are not linear, which indicates that the adsorption process is controlled in different stages. The adsorption of MB and RO16 by MR-LDH was conducted in two stages: initial bulk diffusion, followed by intra-particle diffusion into the pores. The changes in slope for both dyes (from high to low) indicate that the external diffusion was faster and that intra-particle diffusion was the controlling phase68,69. In Table 3, the values of kid and I as well as the correlation coefficient (R2) are given as separate steps in the adsorption process.

Intra-particle diffusion for removing MB and RO16 onto the MR-LDH nanocomposite.

Thermodynamic parameters, including ΔGº, ΔSº, and ΔHº, are also calculated using the following equations [Eqs. (12)–(14)]:

where KD points to the distribution coefficient of the adsorption, R and T are the universal gas constant [8.314 J/(mol·K)] and the temperature (K), respectively.

To examine the thermodynamic behavior of MR-LDH toward MB and RO16 adsorption process, the adsorption process was carried out at diverse temperature values. Using mentioned thermodynamic equations and plotting ln(KD) against 1/T, ΔHº (kJ/mol) was obtained from the slope of the linear graph, and ΔSº (kJ/mol.K) was calculated using the intercept. All numerical data are gathered in Table 4. As can be concluded in the case of MB adsorption, increasing the temperature increases the removal efficiency (98% at 313 K). Therefore, adsorption is an endothermic process. For RO16 adsorption, increasing the temperature is also favorable for the adsorption process and the highest removal efficiency (97%) was obtained at 313 K. This process is endothermic. Notably, the negative values of ΔG° for MB and RO16 adsorption on the MR-Co/Al LDH at varied temperatures demonstrated their spontaneity.

Reusability is an economic factor in adsorption fields on laboratory and industrial scales. Since MR-LDH is a magnetic adsorbent, collecting it with an external magnet is convenient. After washing the collected adsorbent and reusing it four consecutive times, there is the ignorable decline in adsorption efficiency in the performance of MR-LDH, as displayed in Fig. 14. It shows that the collection and washing of the adsorbent can discharge the analyte from the interlayer of MR-LDH, leading to regenerating the sorption sites with high efficiency. Thus, we believe that our adsorbent shows acceptable reusability in repetitive cycles.

Reusability of MR-LDH for RO16 and MB adsorption.

Since it has been estimated that 12% of dyes are wasted during the production process, numerous adsorbents were presented to eliminate the dye molecules from environmental wastewater. Herein, we compare our proposal adsorbent, MR-Co/Al LDH, with previous reports to highlight the benefits of present works. All the caparisoned items are shown in Table 5. As can be seen, our material is superior compared to those reported earlier. In addition to the optimum adsorption conditions, our adsorbent takes advantage of the magnetic property. Therefore, an external magnetic field can easily separate them from the solution after the adsorption. Thus, it can be favorable for a reusability strategy.

Summarily, a magnetic core–shell, namely MR-LDH, was synthesized as previously reported. Removal of organic dyes has become a worldwide challenge as a result of arising various human diseases. The as-prepared material was exposed to the removal of two organic dyes, MB and RO16, which had an adsorption capacity of 54.01 and 53.04 mg/g, respectively. The primary parameters affecting the adsorption process were optimized, including pH, contact duration, and adsorbent dose. Then, the modeling calculations were performed to provide a better understanding of adsorption mechanisms. Accordingly, the Langmuir isotherm was well fitted with both dyes adsorption experiments demonstrating the monolayer adsorption process. Additionally, the pseudo-second-order model provided the best model of the adsorption kinetics of both dyes. Lastly, reusability is essential for realizing efficient, economical, and environmentally friendly adsorbents. Since an external magnet can effortlessly collect the magnetic adsorbent, it provides a facile platform for eliminating dyes from wastewater which is required to expand appropriate cases in the social application.

All data generated or analyzed data for experimental part during this study are included in this published article. The data that support the findings of this study are available from the corresponding author, [Asiyeh kheradmand], upon reasonable request. Moreover, all other data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.

Shayesteh, H., Ashrafi, A. & Rahbar-Kelishami, A. Evaluation of Fe3O4@MnO2 core-shell magnetic nanoparticles as an adsorbent for decolorization of methylene blue dye in contaminated water: Synthesis and characterization, kinetic, equilibrium, and thermodynamic studies. J. Mol. Struct. 1149, 199–205 (2017).

Article ADS CAS Google Scholar

Eltaweil, A. S., Elgarhy, G. S., El-Subruiti, G. M. & Omer, A. M. Carboxymethyl cellulose/carboxylated graphene oxide composite microbeads for efficient adsorption of cationic methylene blue dye. Int. J. Biol. Macromol. 154, 307–318 (2020).

Article CAS PubMed Google Scholar

Shi, Z., Wang, Y., Sun, S., Zhang, C. & Wang, H. Removal of methylene blue from aqueous solution using Mg-Fe, Zn-Fe, Mn-Fe layered double hydroxide. Water Sci. Technol. 81, 2522–2532 (2020).

Article CAS PubMed Google Scholar

Parmar, B., Bisht, K. K., Rajput, G. & Suresh, E. Recent advances in metal-organic frameworks as adsorbent materials for hazardous dye molecules. Dalton Trans. 50, 3083–3108 (2021).

Article CAS PubMed Google Scholar

Xiao, W. et al. Adsorption of organic dyes from wastewater by metal-doped porous carbon materials. J. Clean. Prod. 284, 124773 (2021).

Article CAS Google Scholar

Al-Musawi, T. J., McKay, G., Rajiv, P., Mengelizadeh, N. & Balarak, D. Efficient sonophotocatalytic degradation of acid blue 113 dye using a hybrid nanocomposite of CoFe2O4 nanoparticles loaded on multi-walled carbon nanotubes. J. Photochem. Photobiol. A 424, 113617 (2022).

Article CAS Google Scholar

Yilmaz, M., Mengelizadeh, N., Saloot, M. K., Shahbaksh, S. & Balarak, D. Facile synthesis of Fe3O4/ZnO/GO photocatalysts for decolorization of acid blue 113 under solar, visible and UV lights. Mater. Sci. Semicond. Process. 144, 106593 (2022).

Article CAS Google Scholar

Al-Musawi, T. J., Mengelizadeh, N., Al-Rawi, O. & Balarak, D. Capacity and modeling of acid blue 113 dye adsorption onto chitosan magnetized by Fe2O3 nanoparticles. J. Polym. Environ. 30, 344–359 (2022).

Article CAS Google Scholar

Balarak, D., Zafariyan, M., Igwegbe, C. A., Onyechi, K. K. & Ighalo, J. O. Adsorption of acid blue 92 dye from aqueous solutions by single-walled carbon nanotubes: isothermal, kinetic, and thermodynamic studies. Environ. Process. 8, 869–888 (2021).

Article CAS Google Scholar

Al-Musawi, T. J., Mengelizadeh, N., Taghavi, M., Shehu, Z. & Balarak, D. Capability of copper–nickel ferrite nanoparticles loaded onto multi-walled carbon nanotubes to degrade acid blue 113 dye in the sonophotocatalytic treatment process. Environ. Sci. Pollut. Res. https://doi.org/10.1007/s11356-022-19460-z (2022).

Article Google Scholar

Uddin, M. J., Ampiaw, R. E. & Lee, W. Adsorptive removal of dyes from wastewater using a metal-organic framework: A review. Chemosphere 284, 131314 (2021).

Article ADS CAS PubMed Google Scholar

Yeow, P. K., Wong, S. W. & Hadibarata, T. Removal of azo and anthraquinone dye by plant biomass as adsorbent – A review. Biointerface Res. Appl. Chem. 11, 8218–8232 (2021).

CAS Google Scholar

Panda, S. K. et al. Magnetite Nanoparticles as Sorbents for Dye Removal: a Review. Environmental Chemistry Letters vol. 19 (Springer International Publishing, 2021).

Nithya, R., Thirunavukkarasu, A., Sathya, A. B. & Sivashankar, R. Magnetic materials and magnetic separation of dyes from aqueous solutions: a review. Environ. Chem. Lett. 19, 1275–1294 (2021).

Article CAS Google Scholar

Khadir, A., Negarestani, M., kheradmand, A., Azad, A. & Sillanpää, M. The utilization of biomaterials for water purification: Dyes, heavy metals, and pharmaceuticals BT - Novel materials for dye-containing wastewater treatment. in (eds. Muthu, S. S. & Khadir, A.) 27–58 (Springer Singapore, 2021). https://doi.org/10.1007/978-981-16-2892-4_2.

Negarestani, M., Etemadifar, P. & Kheradmand, A. A mini-review on the application of magnetic-based MOF for dye elimination from polluted Waters BT - Advanced removal techniques for dye-containing wastewaters. in (eds. Muthu, S. S. & Khadir, A.) 57–69 (Springer Singapore, 2021). https://doi.org/10.1007/978-981-16-3164-1_3.

Yao, X. et al. Magnetic activated biochar nanocomposites derived from wakame and its application in methylene blue adsorption. Biores. Technol. 302, 122842 (2020).

Article CAS Google Scholar

Santoso, E. et al. Review on recent advances of carbon based adsorbent for methylene blue removal from waste water. Materials Today Chemistry 16, 100233 (2020).

Article CAS Google Scholar

Malek, N. N. A., Jawad, A. H., Ismail, K., Razuan, R. & Al-Othman, Z. A. Fly ash modified magnetic chitosan-polyvinyl alcohol blend for reactive orange 16 dye removal: Adsorption parametric optimization. Int. J. Biol. Macromol. 189, 464–476 (2021).

Article CAS PubMed Google Scholar

Tsade Kara, H., Anshebo, S. T., Sabir, F. K. & Adam Workineh, G. Removal of methylene blue dye from wastewater using periodiated modified nanocellulose. Int. J. Chem. Eng. 2021, (2021).

Batool, A. & Valiyaveettil, S. Chemical transformation of soya waste into stable adsorbent for enhanced removal of methylene blue and neutral red from water. J. Environ. Chem. Eng. 9, 104902 (2021).

Article CAS Google Scholar

Elkhider, K. H. A. et al. Synthesis, characterization and dye adsorption performance of strontium ferrite decorated bentonite-CoNiAl magnetic composite. Arab. J. Sci. Eng. 45, 7397–7408 (2020).

Article CAS Google Scholar

Jalilvand, P., Rahbar-Kelishami, A., Mohammadi, T. & Shayesteh, H. Optimizing of malachite green extraction from aqueous solutions using hydrophilic and hydrophobic nanoparticles. J. Mol. Liq. 308, 113014 (2020).

Article CAS Google Scholar

Shindhal, T. et al. A critical review on advances in the practices and perspectives for the treatment of dye industry wastewater. Bioengineered 12, 70–87 (2021).

Article CAS PubMed Google Scholar

Kubra, K. T., Salman, M. S. & Hasan, M. N. Enhanced toxic dye removal from wastewater using biodegradable polymeric natural adsorbent. J. Mol. Liq. 328, 115468 (2021).

Article CAS Google Scholar

Raji, F., Shayesteh, H. & Rahbar-Kelishami, A. Y-Y microfluidic polymer/salt aqueous two-phase system for optimization of dye extraction: Evaluation of channel geometry. Sep. Sci. Technol. (Phila.) https://doi.org/10.1080/01496395.2022.2059677 (2022).

Article Google Scholar

Zubair, M., Ihsanullah, I., Abdul Aziz, H., Azmier Ahmad, M. & Al-Harthi, M. A. Sustainable wastewater treatment by biochar/layered double hydroxide composites: Progress, challenges, and outlook. Biores. Technol. 319, 124128 (2021).

Article CAS Google Scholar

Gunasegaran, M., Ravi, S. & Shoparwe, N. F. Kinetic studies of reactive orange 16 (RO16) dye removal from aqueous solution using PIMs. J. Phys. Conf. Ser. 1529, (2020).

Lee, L. Z. & Zaini, M. A. A. Equilibrium and kinetic adsorption studies of reactive orange onto resorcinol-formaldehyde carbon gel. Chem. Eng. Trans. 56, 811–816 (2017).

Google Scholar

Dutta, S., Gupta, B., Srivastava, S. K. & Gupta, A. K. Recent advances on the removal of dyes from wastewater using various adsorbents: A critical review. Mater. Adv. 2, 4497–4531 (2021).

Article CAS Google Scholar

Rahman-Setayesh, M. R., Rahbar-Kelishami, A. & Shayesteh, H. Equilibrium, kinetic, thermodynamic applications for methylene blue removal using Buxus sempervirens leaf powder as a powerful low-cost adsorbent. J. Part. Sci. Technol. 5, 161–170 (2019).

CAS Google Scholar

Jawad, A. H., Malek, N. N. A., Abdulhameed, A. S. & Razuan, R. Synthesis of magnetic chitosan-Fly Ash/Fe3O4 composite for adsorption of reactive orange 16 dye: Optimization by box-behnken design. J. Polym. Environ. 28, 1068–1082 (2020).

Article CAS Google Scholar

Tran, H. V., Hoang, L. T. & Huynh, C. D. An investigation on kinetic and thermodynamic parameters of methylene blue adsorption onto graphene-based nanocomposite. Chem. Phys. 535, 110793 (2020).

Article CAS Google Scholar

Abdulhameed, A. S., Mohammad, A. K. T. & Jawad, A. H. Application of response surface methodology for enhanced synthesis of chitosan tripolyphosphate/TiO2 nanocomposite and adsorption of reactive orange 16 dye. J. Clean. Prod. 232, 43–56 (2019).

Article CAS Google Scholar

Silva, A. F. da, Duarte, J. L. da S. & Meili, L. Different routes for MgFe/LDH synthesis and application to remove pollutants of emerging concern. Sep. Purif. Technol. 264, (2021).

Normah, N. et al. Size selectivity of anionic and cationic dyes using LDH modified adsorbent with low-cost rambutan peel to hydrochar. Bull. Chem. React. Eng. Catal. 16, 869–880 (2021).

Article CAS Google Scholar

Jijoe, P. S., Yashas, S. R. & Shivaraju, H. P. Fundamentals, synthesis, characterization and environmental applications of layered double hydroxides: a review. Environ. Chem. Lett. 19, 2643–2661 (2021).

Article CAS Google Scholar

Poudel, M. B., Awasthi, G. P. & Kim, H. J. Novel insight into the adsorption of Cr(VI) and Pb(II) ions by MOF derived Co-Al layered double hydroxide @hematite nanorods on 3D porous carbon nanofiber network. Chem. Eng. J. 417, (2021).

Johnston, A. L., Lester, E., Williams, O. & Gomes, R. L. Understanding Layered Double Hydroxide properties as sorbent materials for removing organic pollutants from environmental waters. J. Environ. Chem. Eng. 9, 105197 (2021).

Article CAS Google Scholar

Chaillot, D., Bennici, S. & Brendlé, J. Layered double hydroxides and LDH-derived materials in chosen environmental applications: A review. (2020).

Lesbani, A., Siregar, P. M. S. B. N., Palapa, N. R., Taher, T. & Riyanti, F. Adsorptive removal methylene-blue using zn/al ldh modified rice husk biochar. Pol. J. Environ. Stud. 30, 3117–3124 (2021).

Article CAS Google Scholar

Sharma, R., Arizaga, G. G. C., Saini, A. K. & Shandilya, P. Layered double hydroxide as multifunctional materials for environmental remediation: from chemical pollutants to microorganisms. Sustain. Mater. Technol. 29, e00319 (2021).

CAS Google Scholar

Negarestani, M., Farimaniraad, H., Mollahosseini, A., Kheradmand, A. & Shayesteh, H. Facile preparation of sisal–Fe/Zn layered double hydroxide bio-nanocomposites for the efficient removal of rifampin from aqueous solution: kinetic, equilibrium, and thermodynamic studies. Int. J. Phytoremed. https://doi.org/10.1080/15226514.2022.2093834 (2022).

Article Google Scholar

Kheradmand, A., Ghiasinejad, H., Javanshir, S., Khadir, A. & Jamshidi, E. Efficient removal of Ibuprofen via novel core – shell magnetic bio-surfactant rhamnolipid – layered double hydroxide nanocomposite. J. Environ. Chem. Eng. 9, 106158 (2021).

Article CAS Google Scholar

Sriram, G. et al. Surface engineering of silica based materials with Ni–Fe layered double hydroxide for the efficient removal of methyl orange: Isotherms, kinetics, mechanism and high selectivity studies. Chemosphere 287, 131976 (2022).

Article ADS CAS PubMed Google Scholar

Belviso, C., Piancastelli, A., Sturini, M. & Belviso, S. Synthesis of composite zeolite-layered double hydroxides using ultrasonic neutralized red mud. Microporous Mesoporous Mater. 299, 110108 (2020).

Article CAS Google Scholar

Nazir, M. A. et al. Journal of molecular liquids. Appl. Clay Sci. 190, 105564 (2020).

Article CAS Google Scholar

Rasheed, T. et al. Surfactants-based remediation as an effective approach for removal of environmental pollutants—A review. J. Mol. Liq. 318, 113960 (2020).

Article CAS Google Scholar

da Silva, V. L. et al. Rhamnolipid from Pseudomonas aeruginosa can improve the removal of Direct Orange 2GL in textile dye industry effluents. J. Mol. Liq. 321, 114753 (2021).

Article CAS Google Scholar

Liu, Y. et al. Heterogeneous Fenton-like catalyst for treatment of rhamnolipid-solubilized hexadecane wastewater. Chemosphere 236, 124387 (2019).

Article ADS CAS PubMed Google Scholar

Tiso, T. et al. Integration of genetic and process engineering for optimized rhamnolipid production using pseudomonas putida. Front. Bioeng. Biotechnol. 8, 1–24 (2020).

Article Google Scholar

Lesbani, A., Asri, F., Palapa, N. R., Taher, T. & Rachmat, A. Efficient removal of methylene blue by adsorption using composite based Ca/Al layered double hydroxide-biochar. Global NEST J. 22, 250–257 (2020).

CAS Google Scholar

Rathee, G. et al. A new biocompatible ternary Layered Double Hydroxide Adsorbent for ultrafast removal of anionic organic dyes. Sci. Rep. 9, 1–14 (2019).

Article CAS Google Scholar

Pan, X. et al. Adsorption behavior and mechanism of acid orange 7 and methylene blue on self-assembled three-dimensional MgAl layered double hydroxide: Experimental and DFT investigation. Appl. Surf. Sci. 522, 146370 (2020).

Article CAS Google Scholar

Mittal, J. Recent progress in the synthesis of Layered Double Hydroxides and their application for the adsorptive removal of dyes: A review. J. Environ. Manage. 295, 113017 (2021).

Article CAS PubMed Google Scholar

Shayesteh, H., Raji, F. & Kelishami, A. R. Influence of the alkyl chain length of surfactant on adsorption process: A case study. Surf. Interfaces 22, 100806 (2021).

Article CAS Google Scholar

Wan, X., Zhan, Y., Long, Z., Zeng, G. & He, Y. Core@double-shell structured magnetic halloysite nanotube nano-hybrid as efficient recyclable adsorbent for methylene blue removal. Chem. Eng. J. 330, 491–504 (2017).

Article CAS Google Scholar

Shayesteh, H., Nodehi, R. & Rahbar-Kelishami, A. Trimethylamine functionalized clay for highly efficient removal of diclofenac from contaminated water: Experiments and theoretical calculations. Surf. Interfaces 20, 100615 (2020).

Article CAS Google Scholar

Jawad, A. H., Rashid, R. A., Ishak, M. A. M. & Wilson, L. D. Adsorption of methylene blue onto activated carbon developed from biomass waste by H2SO4 activation: kinetic, equilibrium and thermodynamic studies. Desalin. Water Treat. 57, 25194–25206 (2016).

Article CAS Google Scholar

Aichour, A., Zaghouane-Boudiaf, H., Iborra, C. V. & Polo, M. S. Bioadsorbent beads prepared from activated biomass/alginate for enhanced removal of cationic dye from water medium: Kinetics, equilibrium and thermodynamic studies. J. Mol. Liq. 256, 533–540 (2018).

Article CAS Google Scholar

Ghaedi, M., Khajehsharifi, H., Yadkuri, A. H., Roosta, M. & Asghari, A. Oxidized multiwalled carbon nanotubes as efficient adsorbent for bromothymol blue. Toxicol. Environ. Chem. 94, 873–883 (2012).

Article CAS Google Scholar

Dana, F., Soleimannejad, J., Moghzi, F., Taherzade, S. D. & Janczak, J. A new stable and reusable nanoscale Cu(II) coordination polymer as an efficient dye adsorbent. Inorg. Chim. Acta 509, 119716 (2020).

Article CAS Google Scholar

Inyinbor, A. A., Adekola, F. A. & Olatunji, G. A. Kinetics, isotherms and thermodynamic modeling of liquid phase adsorption of Rhodamine B dye onto Raphia hookerie fruit epicarp. Water Resour. Ind. 15, 14–27 (2016).

Article Google Scholar

Abdel-Khalek, M. A., Abdel Rahman, M. K. & Francis, A. A. Exploring the adsorption behavior of cationic and anionic dyes on industrial waste shells of egg. J. Environ. Chem. Eng. 5, 319–327 (2017).

Article CAS Google Scholar

Gong, R. et al. Adsorptive removal of methyl orange and methylene blue from aqueous solution with finger-citron-residue-based activated carbon. Ind. Eng. Chem. Res. 52, 14297–14303 (2013).

Article CAS Google Scholar

Marrakchi, F., Khanday, W. A., Asif, M. & Hameed, B. H. Cross-linked chitosan/sepiolite composite for the adsorption of methylene blue and reactive orange 16. Int. J. Biol. Macromol. 93, 1231–1239 (2016).

Article CAS PubMed Google Scholar

Ma, Q. & Wang, L. Adsorption of Reactive blue 21 onto functionalized cellulose under ultrasonic pretreatment: Kinetic and equilibrium study. J. Taiwan Inst. Chem. Eng. 50, 229–235 (2015).

Article CAS Google Scholar

Mane, V. S. & Vijay Babu, P. V. Kinetic and equilibrium studies on the removal of Congo red from aqueous solution using Eucalyptus wood (Eucalyptus globulus) saw dust. J. Taiwan Inst. Chem. Eng. 44, 81–88 (2013).

Article CAS Google Scholar

Noorimotlagh, Z., Soltani, R. D. C., Khataee, A. R., Shahriyar, S. & Nourmoradi, H. Adsorption of a textile dye in aqueous phase using mesoporous activated carbon prepared from Iranian milk vetch. J. Taiwan Inst. Chem. Eng. 45, 1783–1791 (2014).

Article CAS Google Scholar

Kaur, H., Singh, S. & Pal, B. Impact of g-C3N4 loading on NiCo LDH for adsorptive removal of anionic and cationic organic pollutants from aqueous solution. Korean J. Chem. Eng. 38, 1248–1259 (2021).

Article CAS Google Scholar

Mokhtar, A. et al. Adsorption behavior of cationic and anionic dyes on magadiite-chitosan composite beads. Carbohyd. Polym. 229, 115399 (2020).

Article CAS Google Scholar

Usgodaarachchi, L., Thambiliyagodage, C., Wijesekera, R. & Bakker, M. G. Synthesis of mesoporous silica nanoparticles derived from rice husk and surface-controlled amine functionalization for efficient adsorption of methylene blue from aqueous solution. Curr. Res. Green Sustain. Chem. 4, 100116 (2021).

Article CAS Google Scholar

Arora, C. et al. Iron based metal organic framework for efficient removal of methylene blue dye from industrial waste. J. Mol. Liq. 284, 343–352 (2019).

Article CAS Google Scholar

Ramutshatsha-Makhwedzha, D., Mavhungu, A., Moropeng, M. L. & Mbaya, R. Activated carbon derived from waste orange and lemon peels for the adsorption of methyl orange and methylene blue dyes from wastewater. Heliyon 8, e09930 (2022).

Article PubMed PubMed Central Google Scholar

Gowda, S. A. M., Goveas, L. C. & Dakshayini, K. Adsorption of methylene blue by silver nanoparticles synthesized from Urena lobata leaf extract: Kinetics and equilibrium analysis. Mater. Chem. Phys. 288, 126431 (2022).

Article CAS Google Scholar

Fungaro, D. A., Borrely, S. I. & Carvalho, T. E. M. Surfactant modified zeolite from cyclone ash as adsorbent for removal of reactive orange 16 from aqueous solution. Am. J. Environ. Protect. 1, 1–9 (2013).

Article CAS Google Scholar

Chandarana, H., Subburaj, S., Kumar, P. S. & Kumar, M. A. Evaluation of phase transfer kinetics and thermodynamic equilibria of Reactive Orange 16 sorption onto chemically improved Arachis hypogaea pod powder. Chemosphere 276, 130136 (2021).

Article ADS CAS PubMed Google Scholar

Wong, S. Y., Tan, Y. P., Abdullah, A. H. & Ong, S. T. The removal of basic and reactive dyes using quartenised sugar cane bagasse. J. Phys. Sci. 20, 59–74 (2009).

CAS Google Scholar

Akbar-Ali, A. M. et al. Removal of Reactive Orange 16 by adsorption onto activated carbon prepared from rice husk ash: statistical modelling and adsorption kinetics. Sep. Sci. Technol. (Phila.) 55, 26–34 (2020).

Article CAS Google Scholar

Seyedi, M. S., Sohrabi, M. R., Motiee, F. & Mortazavinik, S. Synthesis and characterization of activated carbon@zerovalent iron–nickel nanoadsorbent for highly efficient removal of Reactive Orange 16 from aqueous sample: experimental design, kinetic, isotherm and thermodynamic studies. Res. Chem. Intermed. 46, 1645–1662 (2020).

Article CAS Google Scholar

Download references

Department of Civil and Environmental Engineering, Iran University of Science and Technology, Tehran, Iran

Asiyeh Kheradmand, Mehrdad Negarestani & Hossein Ghiasinejad

Department of Chemistry, Iran University of Science and Technology, Tehran, Iran

Sima Kazemi

School of Chemical, Petroleum and Gas Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran

Hadi Shayesteh

Pharmaceutical and Heterocyclic Compounds Research Laboratory, Chemistry Department, Iran University of Science and Technology, Tehran, Iran

Shahrzad Javanshir

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

A.k.: Experimental work, Methodology, Software, Writing original draft.M.N.: Experimental work, Methodology, Software, Writing original draft.S.K.: Software, Writing - review and editing.H.S.: Software, Writing - review and editing.H.G.: Conceptualization, Methodology, Writing - review and editing, Supervision.S.J.: Conceptualization, Methodology, Writing - review and editing, Supervision.All authors reviewed the manuscript.

Correspondence to Asiyeh Kheradmand or Shahrzad Javanshir.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Kheradmand, A., Negarestani, M., Kazemi, S. et al. Adsorption behavior of rhamnolipid modified magnetic Co/Al layered double hydroxide for the removal of cationic and anionic dyes. Sci Rep 12, 14623 (2022). https://doi.org/10.1038/s41598-022-19056-0

Download citation

Received: 17 April 2022

Accepted: 23 August 2022

Published: 26 August 2022

DOI: https://doi.org/10.1038/s41598-022-19056-0

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Scientific Reports (2023)

Scientific Reports (2023)

International Journal of Environmental Science and Technology (2023)

Environmental Science and Pollution Research (2023)

Journal of Polymers and the Environment (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.